martempering
a heat treatment involving austenitisation followed by step quenching, at a rate fast enough to avoid the formation of ferrite, pearlite or bainite to a temperature slightly above the Ms point. Soaking must be long enough to avoid the formation of bainite. The advantage of martempering is the reduction of thermal stresses compared to normal quenching. This prevents cracking and minimises distortion.

Mechanics glossary. 2013.

Look at other dictionaries:

  • Martempering — is a heat treatment for steel involving austenitisation followed by step quenching, at a rate fast enough to avoid the formation of ferrite, pearlite or bainite to a temperature slightly above the martensite start (Ms) point. Soaking must be long …   Wikipedia

  • Martempering — Martempering. См. Мартенситная закалка. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • martempering — /mahr tem peuhr ing/, n. Metall. a quenching process used to harden austenitic steel. [1940 45; MAR(TENSITE) + TEMPER + ING1] * * * …   Universalium

  • martempering — mar·tempering …   English syllables

  • martempering — E una forma di tempra interrotta nel quale l acciaio è rapidamente raffreddato dalla temperatura di austenitizzazione fino ad una temperatura leggermente superiore ad Ms, mantenuto a tale temperatura finché la temperatura non è omogenea su tutto… …   Glossario di Metallurgia

  • martempering — ˈmär+ˌ noun ( s) Etymology: martensite + tempering : the process of quenching steel from above the transformation temperature in a bath at about 350° F and then cooling to room temperature after the temperature has become nearly uniform with the… …   Useful english dictionary

  • Мартенситная закалка — Martempering Мартенситная закалка. (1) Упрочняющий технологический процесс, в котором находящийся в аустенитном состоянии материал на железной основе охлаждается в соответствующей среде при температуре чуть выше температуры начала мартенситного… …   Словарь металлургических терминов

  • Carbon steel — Iron alloy phases Ferrite (α iron, δ iron) Austenite (γ iron) Pearlite (88% ferrite, 12% cementite) …   Wikipedia

  • Molten salt — Molten FLiBe (2LiF BeF2) Molten salt refers to a salt that is in the liquid phase that is normally a solid at standard temperature and pressure (STP). A salt which is normally liquid at STP is usually called a room temperature ionic liquid,… …   Wikipedia

  • Закалка на мартенсит — Marquenching Закалка на мартенсит. См. Martempering Мартенситную закалку. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.